400 Series Stainless Steel
410 / 410 Heat Treated
Details
- CA15
- ASTM A743
-
Mechanical Properties
Hardness 207 HB typical Tensile 90 ksi min Yield 65 ksi min - Also stocking heat treated material
- 28-32 RC
- 38-42 RC
410 Stainless Steel (ASTM A743)
Grade 410 stainless steel is a martensitic stainless steel which contains ~12.75% chromium, offering both exceptional wear and corrosion resistance. Heat treating yields improvements in hardness as well as corrosion resistance.
At Texcellent Industries, we have many sizes of 410 stainless in stock, including heat treated to both 28-32 RC and 38-42 RC.
Stocking tubing sizes up to 31.5 inch OD with up to 4.25 inch wall thickness.
Call or email today with your specific needs.
| ASTM A743 specs | |
|---|---|
| 410 CA15 | |
| Carbon (% max) | 0.15 |
| Manganese (% max) | 1.00 |
| Silicon (% max) | 1.50 |
| Phosphorus (% max) | 0.04 |
| Sulfur (% max) | 0.04 |
| Chromium (%) | 11.5 – 14.0 |
| Nickel (%) | 1.00 |
| Molybdenum (% max) | 0.50 |
416 / 416 Heat Treated
Details
- CA15
- UNS S41600
-
Mechanical Properties
Hardness 212 HB typical Tensile 80 ksi min Yield 40 ksi min - Also stocking heat treated material
- 28-32 RC
- 38-42 RC
416 Stainless Steel (UNS S41600)
Grade 416 stainless steel is a martensitic stainless steel similar to type 410. Grade 416 is free machining and is the most easily machined stainless steel. Grade 416 can be hardened similarly to other 400 series stainless steels.
At Texcellent Industries, we have many sizes of 416 stainless in stock, including heat treated to both 28-32 RC and 38-43 RC.
Stocking tubing sizes up to 30 inch OD with up to 3.5 inch wall thickness.
Call or email today with your specific needs.
| UNS S41600 specs | |
|---|---|
| 416 | |
| Carbon (% max) | 0.15 |
| Manganese (% max) | 1.00 |
| Silicon (% max) | 1.50 |
| Phosphorus (% max) | 0.04 |
| Sulfur (% max) | 0.20 |
| Chromium (%) | 12.0 – 14.0 |
| Nickel (%) | 1.00 |
| Molybdenum (% max) | 0.60 |
| Selenium (% max) | 0.30 |
420 / 420F / 420 Heat Treated
Details
- CA40 / CA40F
- ASTM A743
-
Mechanical Properties
Hardness 240 HB typical Tensile 100 ksi min Yield 70 ksi min -
Also stocking heat treated material
- 28–35 RC
- 43–47 RC
420 / 420F Stainless Steel (ASTM A743)
Grade 420 stainless steel is a martensitic stainless steel with similar corrosion properties to type 410. Grade 420 has a higher carbon content allowing for heat treating to higher hardness values and better abrasion resistance, but with a lower impact strength. Type 420F has a higher sulfur content resulting in slightly lower enlongation. Grade 420F is a free machining grade.
At Texcellent Industries, we have many sizes of 420 stainless in stock, including heat treated to both 28-35 RC and 43-47 RC.
Stocking tubing sizes up to 30 inch OD with up to 3.5 inch wall thickness.
Call or email today with your specific needs.
| ASTM A743 specs | ||
|---|---|---|
| 420 CA40 | 420F CA40F | |
| Carbon (%) | 0.20 – 0.40 | 0.20 – 0.40 |
| Manganese (% max) | 1.00 | 1.00 |
| Silicon (% max) | 1.50 | 1.50 |
| Phosphorus (% max) | 0.04 | 0.04 |
| Sulfur (% max) | 0.04 | 0.20 – 0.40 |
| Chromium (%) | 11.5 – 14.0 | 11.5 – 14.0 |
| Nickel (%) | 1.00 | 1.00 |
| Molybdenum (% max) | 0.50 | 0.50 |
440A
Details
- UNS S44002
-
Mechanical Properties
Hardness 240 HB typical Tensile 105 ksi min Yield 60 ksi min
440A Stainless Steel (UNS S44002)
Grade 440A stainless steel is a high carbon martensitic stainless steel. Grade 440A has good strength and excellent hardness. Grade 440A can be hardened up to 56 RC.
At Texcellent Industries, we have many sizes of 440A stainless in stock.
Stocking tubing sizes up to 12.5 inch OD with up to 3.5 inch wall thickness.
Call or email today with your specific needs.
| UNS S44002 specs | |
|---|---|
| 440A | |
| Carbon (%) | 0.60 – 0.75 |
| Manganese (% max) | 1.00 |
| Silicon (% max) | 1.00 |
| Phosphorus (% max) | 0.04 |
| Sulfur (% max) | 0.03 |
| Chromium (%) | 16.0 – 18.0 |
| Nickel (% max) | 0.04 |
| Molybdenum (% max) | 0.75 |
440C
Details
- UNS S44004
-
Mechanical Properties
Hardness 240 HB typical Tensile 110 ksi min Yield 65 ksi min
440C Stainless Steel (UNS S44004)
Grade 440C stainless steel is a high carbon martensitic stainless steel. Grade 440C has good strength and excellent hardness. Grade 440C can be hardened up to 60 RC.
Call or email today with your specific needs.
| UNS S44004 specs | |
|---|---|
| 440C | |
| Carbon (%) | 0.95 – 1.20 |
| Manganese (% max) | 1.00 |
| Silicon (% max) | 1.00 |
| Phosphorus (% max) | 0.04 |
| Sulfur (% max) | 0.03 |
| Chromium (%) | 16.0 – 18.0 |
| Nickel (% max) | 0.05 |
| Molybdenum (% max) | 0.75 |
CA6NM
Details
- CA6NM
- ASTM A743
-
Mechanical Properties
Hardness 285 HB typical Tensile 110 ksi min Yield 80 ksi min
CA6NM Stainless Steel (ASTM A743)
CA6NM stainless steel is a martensitic stainless steel with good corrosion resistance and improved impact strength. CA6NM can be hardened up to 400 HB.
Stocking tubing sizes up to 13.5 inch OD with up to 3 inch wall thickness.
Call or email today with your specific needs.
| A743 specs | |
|---|---|
| CA6NM | |
| Carbon (% max) | 0.06 |
| Manganese (% max) | 1.00 |
| Silicon (% max) | 1.00 |
| Phosphorus (% max) | 0.04 |
| Sulfur (% max) | 0.03 |
| Chromium (%) | 11.5 – 14.0 |
| Nickel (%) | 3.5 – 4.5 |
| Molybdenum (%) | 0.40 – 1.0 |